Oxidation protective silicon carbide coating for C/SiC composite modified by a CHROMIUM SILICIDE (cas 12018-09-6)–chromium carbide outer layer

Add time:07/29/2019    Source:sciencedirect.com

A chromium silicide–chromium carbide (Cr3Si–Cr7C3) outer layer mainly composed of Cr3Si, Cr7C3, and a small amount of Cr3C2 was prepared on a SiC coated carbon fiber reinforced silicon carbide (C/SiC) composite using a Powder Immersion Reaction Assisted Coating (PIRAC) method. The Cr3Si–Cr7C3 outer layer showed folded ridge morphology. The width of the largest microcracks on the outer layer of the Cr3Si–Cr7C3/SiC/SiC coating was only one forth of that on the outer layer of the SiC/SiC/SiC coating. The Cr3Si–Cr7C3/SiC/SiC coating showed significantly enhanced oxidation protection compared to the SiC/SiC/SiC coating. After oxidation for 10 h, the Cr3Si–Cr7C3/SiC/SiC coated composite showed nearly the same failure behavior and residual flexural strength as that of the as-received composite.

We also recommend Trading Suppliers and Manufacturers of CHROMIUM SILICIDE (cas 12018-09-6). Pls Click Website Link as below: cas 12018-09-6 suppliers

Prev:Influence of IR-laser irradiation on α-SiC–CHROMIUM SILICIDE (cas 12018-09-6)s ceramics
Next:Synthesis and oxidation behavior of CHROMIUM SILICIDE (cas 12018-09-6) (Cr3Si) nanorods)