Preparation of LANTHANUM ZIRCONATE (cas 12031-48-0) films with a widely controllable La/Zr ratio by LCVD

Add time:08/03/2019    Source:sciencedirect.com

LANTHANUM ZIRCONATE (cas 12031-48-0) (LZ) films with a controllable La/Zr composition were prepared by laser enhanced chemical vapor deposition (LCVD). The effects of different precursors ratio, i.e. the La(dpm)3/Zr(dpm)4 molar ratio, on composition, crystal structure, morphology and electrical conductivity of films were investigated. The formation region of columnar and purely cubic pyrochlore structured LZ films with a controllable La/Zr molar ratio in a wide range of 0.51–2.53 was mapped. Crystal structure changed with the different precursor's ratio, which was caused by atomic substitution between lanthanum and zirconium, being proved by combining with experimental and theoretical XRD patterns. It is found that electrical conductivity of non-stoichiometric LZ films is up to 4.3 × 10−3 S cm−1 at 1073 K. The columnar pyrochlore structured LZ films with a wide region of non-stoichiometric compositions are expected to be candidates for many potential applications, such as dielectric, thermal barrier coatings and nuclear waste treatment materials.

We also recommend Trading Suppliers and Manufacturers of LANTHANUM ZIRCONATE (cas 12031-48-0). Pls Click Website Link as below: cas 12031-48-0 suppliers

Prev:Exceptionally high fracture toughness of carbon nanotube reinforced plasma sprayed LANTHANUM ZIRCONATE (cas 12031-48-0) coatings
Next:A novel long-life cerium LANTHANUM ZIRCONATE (cas 12031-48-0) thermal barrier coating controlled by designed portholes)