Comparison of the oxidation behavior of a Zirconium nitride (cas 12033-93-1) coating in water vapor and air at high temperature

Add time:08/01/2019    Source:sciencedirect.com

The oxidation behavior of Zirconium nitride (cas 12033-93-1) coating in high-temperature water vapor and air environments was studied. The parabolic rate constant of ZrN oxidizing in the water vapor environment at 600 °C was approximately 100 times faster than that in air, due to the larger pores and greater number of cracks that were formed across ZrO2 oxide layer formed during the water vapor oxidation process than during the air oxidation process. A bilayer-structure ZrO2 with tetragonal ZrO2 near the ZrN/ZrO2 interface and monoclinic ZrO2 approaching the outer ZrO2 surface were formed in both cases. The lateral cracks across the ZrO2 scale were caused by volume expansion from the tetragonal ZrO2 phase to the monoclinic ZrO2 phase transition.

We also recommend Trading Suppliers and Manufacturers of Zirconium nitride (cas 12033-93-1). Pls Click Website Link as below: cas 12033-93-1 suppliers

Prev:Sputtering deposition and characterization of Zirconium nitride (cas 12033-93-1) and oxynitride films
Next:First-principles study of fission gas incorporation and migration in Zirconium nitride (cas 12033-93-1))