Enhancement of reaction-sintering of alumina-excess MAGNESIUM ALUMINATE (cas 12068-51-8) spinel in presence of titania

Add time:08/03/2019    Source:sciencedirect.com

Alumina-excess MAGNESIUM ALUMINATE (cas 12068-51-8) spinel finds use in different high temperature applications including steel ladles. Alumina-excess spinel was prepared by solid oxide reaction using magnesia (MgO=10 wt%) and calcined alumina (Al2O3 = 90 wt%), in the sintering temperature range of 1500–1700 °C. The role of titania on the densification, spinelisation, evolution of microstructure and phase assemblage was investigated in this MgO-Al2O3 system. Titania addition increased the rate of densification 20x compared to undoped composition at 1500 °C under dynamic heating condition. However, under static firing, the beneficial effect of titania on densification could only be discerned at lower temperatures. The microstructure of titania doped sintered alumina-excess spinel compacts contain magnesium aluminium titanate phase in the grain boundary of corundum and spinel grains. The beneficial effect of titania on densification is attributed to magnesium aluminium titanate phase (MgxAl2(1-x)Ti(1+x)O5) development and also by incorporation of Ti4+ into the spinel structure.

We also recommend Trading Suppliers and Manufacturers of MAGNESIUM ALUMINATE (cas 12068-51-8). Pls Click Website Link as below: cas 12068-51-8 suppliers

Prev:The effects of in situ formation of Y3Al5O12 on property improvement of MAGNESIUM ALUMINATE (cas 12068-51-8) spinel refractories
Next:Densification and microstructure of MAGNESIUM ALUMINATE (cas 12068-51-8) spinel for adding method of Sc2O3)