Color tunable photoluminescence properties in Eu3+ doped calcium bismuth vanadate phosphors for luminescent devices

Add time:08/01/2019    Source:sciencedirect.com

Single phase Eu3+ activated calcium bismuth vanadate (CaBiVO5) phosphors have been successfully synthesized using solid state reaction method. X-ray diffraction (XRD) analysis confirms the pure phase formation and scanning electron microscope (SEM) micrographs exhibit inhomogeneous particle formation with irregular morphology of Eu3+ doped CaBiVO5 (CBV) phosphor. The photoluminescence excitation (PLE) spectrum indicates significant absorption in the ultraviolet (UV) and near ultraviolet (n-UV) spectral region for un-doped CBV sample, whereas Eu3+ doped CBV phosphors reveal various sharp absorption bands in n-UV and blue region along with host absorption bands. Trivalent europium activated CBV phosphors under 342 nm excitation exhibit dominant red emission peak at 613 nm wavelength accompanied by weak broadband originating from VO4 groups, whereas the phosphors under 464 nm excitation, exhibit similar emission profile with most intense one centered at 613 nm by excluding host emission bands. The energy transfer mechanisms and the probable cause for concentration quenching beyond 4.0 mol% of Eu3+ ions concentration have been discussed in detail. The CIE chromaticity coordinates for the optimized phosphor, (0.551, 0.398) and (0.639, 0.358), situated in the reddish-orange and red region under 342 and 464 nm excitations, respectively. The CIE coordinates calculated based on the emission spectra measured under 464 nm excitation are close to the commercial phosphor Y2O2S: Eu3+ (x = 0.622 and y = 0.351). All the above mentioned results support the utilization of Eu3+ doped CBV phosphor as a potential red emitting component for luminescent devices.

We also recommend Trading Suppliers and Manufacturers of CALCIUM VANADATE (cas 12135-52-3). Pls Click Website Link as below: cas 12135-52-3 suppliers

Prev:Eu and Cu co-substituted CALCIUM VANADATE (cas 12135-52-3) — The crystal structure, luminescence and color
Next:Enhancement of the activity for oxidative dehydrogenation of propane on calcium hydroxyapatite substituted with vanadate)