Synthesis, characterization, and high gas permeability of poly(diarylacetylene)s having fluorenyl groups

Add time:08/06/2019    Source:sciencedirect.com

Diarylacetylenes having fluorenyl groups and other substituents (trimethylsilyl, t-butyl, bromine, fluorine) (1a–1) were polymerized with TaCl5–n-Bu4Sn. Monomers 1a–l produced high molecular weight polymers 2a–l (Mw 5.1 × 105–1.3 × 106) in 12–59% yields. All of the polymers were soluble in common organic solvents, and gave tough free-standing membranes by the solution casting method. The onset temperatures of weight loss of polymers 2a–l in air were over 400 °C, indicating considerably high thermal stability. All the polymer membranes showed high gas permeability; e.g., the oxygen permeability coefficient (PO2) of 2a was as large as 4800 barrers. Membrane 2d possessing two fluorine atoms at meta and para positions of the phenyl ring showed the highest oxygen permeability (PO2 = 6600 barrers) among the present polymers.

We also recommend Trading Suppliers and Manufacturers of Bis-(fluorenyl)-zirconium dichloride (cas 12149-83-6). Pls Click Website Link as below: cas 12149-83-6 suppliers

Prev:Photolysis of chloride precursors as a method to prepare and characterize the triplet state of fluorenyl-substituted m-xylylene diradicals
Next:Biphenyl- and fluorenyl-based potential molecular electronic devices)