The role of the Austenite (cas 12244-31-4) grain size in the martensitic transformation in low carbon steels

Add time:08/10/2019    Source:sciencedirect.com

There is sufficient experimental evidence to propose that the formation kinetics of athermal martensite directly depends on the Austenite (cas 12244-31-4) grain structure from which the martensite forms. Yet, this dependence is frequently ignored. The present study investigates the role of the prior austenite grain size (PAGS) in the martensitic transformation in low-carbon steels. The transformation kinetics was experimentally studied for PAGS in the range from 6 to 185 μm and theoretically analysed based on the nucleation rate and the thermodynamic balance between the chemical driving force and the resistance exerted by the austenite against the progress of the transformation. It is observed that grain refinement shifts the martensite start temperature (MS) to lower values and accelerates the transformation rate at initial stages. At a later stage, when approximately 30% martensite has formed, the transformation rate decreases rapidly for small PAGS, whereas higher rates are maintained in coarse-grained microstructures. The change in martensite formation rate with the grain size depends on the nuclei density and on the austenite strength. This research enables an optimised selection of processing parameters for the design of ultra-high strength steels that require the formation of a controlled fraction of martensite.

We also recommend Trading Suppliers and Manufacturers of Austenite (cas 12244-31-4). Pls Click Website Link as below: cas 12244-31-4 suppliers

Prev:Stabilizing Austenite (cas 12244-31-4) via a core-shell structure in the medium Mn steels
Next:Austenite (cas 12244-31-4) morphology and resistance to hydrogen embrittlement in medium Mn transformation-induced plasticity steel)