Influence of magnesium-to-phosphate ratio and water-to-cement ratio on hydration and properties of magnesium potassium phosphate cements

Add time:08/11/2019    Source:sciencedirect.com

Magnesium-to-phosphate (Mg/PO4) and water-to-cement (w/c) ratios are important factors controlling hydration and properties of magnesium potassium phosphate (MKP) cements. This study investigated the influence of Mg/PO4 molar ratios (2.7, 4 and 8) and w/c (0.25 and 5) on cement hydration, compressive strength and volume stability. Low w/c ratio slowed down cement hydration at lower Mg/PO4 beyond 1 day, and prevented the precipitation of intermediate hydrates at higher Mg/PO4. At lower Mg/PO4 expansion and strength loss were observed with time due to the continuing hydration within the already hardened cement. Higher Mg/PO4 resulted in faster hydration, higher strength, and in the precipitation of traces of brucite, which had no significant influence on the long-term volume stability and strength. Therefore, moderate Mg/PO4 molar ratios between 4 and 8 depending on w/c ratio used are recommended for the production of MKP cements with robust performance.

We also recommend Trading Suppliers and Manufacturers of AMMONIUM MAGNESIUM PHOSPHATE HEXAHYDRATE (cas 13478-16-5). Pls Click Website Link as below: cas 13478-16-5 suppliers

Prev:Infrared and Raman spectra of magnesium ammonium phosphate hexahydrate (struvite) and its isomorphous analogues. V. Spectra of protiated and partially deuterated magnesium ammonium arsenate hexahydrate (arsenstruvite)
Next:Infrared and Raman spectra of magnesium ammonium phosphate hexahydrate (struvite) and its isomorphous analogues. IV. FTIR spectra of protiated and partially deuterated nickel ammonium phosphate hexahydrate and nickel potassium phosphate hexahydrate)