Temperature and pressure dependence of electrical conductivity in synthetic anorthite (cas 1302-54-1)

Add time:08/15/2019    Source:sciencedirect.com

Electrical conductivity measurements of synthetic anorthite were carried out as a function of pressure and temperature by a Solartron-1260 Impedance/Gain phase analyzer in a multi-anvil apparatus. The impedance spectroscopy was performed in a frequency range from 10–1 Hz to 106 Hz. The sample was synthesized at 1673 K in a high temperature furnace. Our experimental results show that (1) a dramatic increase in electrical conductivity with increasing temperature and a slightly decrease in conductivity with increasing pressure at constant temperature, however, the effect of pressure on the conductivity is less pronounced than that of temperature; (2) the activation enthalpy linearly increases with increasing pressure (1.86–1.91 eV) reflecting the mobility of Ca2+ decreases as the anorthite framework becomes more compressed; (3) the activation energy at atmospheric pressure and activation volume are 1.83 eV and 2.39 cm3/mol, respectively; (4) According to these Arrhenius parameters, it is proposed that the possible dominant mechanism of the charge transport in anorthite under experimental conditions is the hopping of Ca2+ from one near aluminum oxygen site to another; (4) the diffusion coefficient of calcium was calculated from the present conductivity data using Nernst–Einstein equation, and compared with previous experimental results.

We also recommend Trading Suppliers and Manufacturers of anorthite (cas 1302-54-1). Pls Click Website Link as below: cas 1302-54-1 suppliers

Prev:Research on the characterization of a porcelainised material fabricated by adding a small amount of anorthite (cas 1302-54-1) chamotte
Next:Production and characterisation of granulated frit to achieve anorthite (cas 1302-54-1) based glass–ceramic glaze)