Production of mono-anorthite (cas 1302-54-1) phase through mechanical activation

Add time:08/19/2019    Source:sciencedirect.com

The structures of kaolinite, calcite and corundum were strongly deteriorated with activating the mixture with high energy planetary mono mill. Anorthite formation kinetics of activated and non-activated mixtures were studied by Differential Thermal Analysis under a heating rate of 5–30 °C, using Kissenger plots. The crystallization of anorthite showed an activation energy of 325 kJ mol−1 for mechanically activated and of 475 kJ mol−1 for non-activated samples. Both specimens crystallized by bulk nucleation. The phase formations were investigated upon heating at 1000–1100–1200–1300 °C. The structure of anorthite, for activated samples, was almost restored after firing at a temperature as low as 1100 °C for which the non-activated samples had to be fired at 1200 °C.

We also recommend Trading Suppliers and Manufacturers of anorthite (cas 1302-54-1). Pls Click Website Link as below: cas 1302-54-1 suppliers

Prev:Development of anorthite (cas 1302-54-1) based white porcelain stoneware tile compositions
Next:OSL dosimetric properties of synthetic Topaz (cas 1302-59-6))