Production of hydrogen from hydrogen sulfide with perovskite type catalysts: LaMO3

Add time:08/16/2019    Source:sciencedirect.com

Catalytic thermal decomposition of 1% (vol.) hydrogen sulfide (H2S) was studied by using perovskite type catalysts within a temperature range between 600 °C and 950 °C and at atmospheric pressure in a quartz tubular reactor, with the aim of producing hydrogen.Lanthanum was selected as an A-site element from the lanthanide series and M: Ce, Co, Cr, Cu, Mo, Sr, V were selected for the B-site in order to build up the perovskite structure as La(M)O3. The influence of different transition metals (Co, Cr, Cu, Mo, V) as well as of alkaline earth (Sr) and of lanthanide (Ce) doping on both catalyst structure and catalytic activity was investigated through catalyst characterization and catalyst activity tests. Structural characterizations of fresh and spent catalysts were performed by XRD and SEM-EDS methods.The most active catalyst was found to be LaCrO3 at 750 °C with a conversion value of 14%, the highest among the seven catalysts at that temperature. Moreover, conversion values such as 5%, and 22% that were achieved at ∼650 °C and ∼825 °C using LaCrO3, were only possible at higher temperatures, 900 °C and 950°C via direct thermal decomposition.La2SrOx fresh sample, had the largest specific surface area, 10.05 m2/g, among the seven catalysts studied, and it gave the highest conversion of 35.7% at 950 °C.

We also recommend Trading Suppliers and Manufacturers of STRONTIUM LANTHANUM SULFIDE (cas 12532-80-8). Pls Click Website Link as below: cas 12532-80-8 suppliers

Prev:An acid-resistant magnetic Nb-substituted crystalline silicotitanate for selective separation of strontium and/or cesium ions from aqueous solution
Next:Relaxor ferroelectricity, ferromagnetic and optical second harmonic properties in lanthanum lithium niobate (La0.05Li0.85NbO3) nanoparticles)