Synthesis and crystallization of new fully renewable resources-based copolyesters: Poly(1,4-Cyclohexanedimethanol (cas 105-08-8)-co-isosorbide 2,5-furandicarboxylate)

Add time:08/13/2019    Source:sciencedirect.com

In this paper, a series of fully biobased poly(1,4-cyclohexanedimethanol-co-isosorbide 2,5-furandicarboxylate)s (PCIsFs) copolyesters have been synthesized from dimethyl-2,5-furandicarboxylate (DMFD), isosorbide (IS) and 1,4-cyclohexanedimethanol (CHDM) by melt polycondensation. The structure of prepared polymers was characterized by 1H NMR and FTIR spectroscopies. Differential scanning calorimetry (DSC) results indicated that the crystallizability and melting temperature (Tm) of PCIsFs can be controlled with the increasing content of isosorbide furanoate units into the copolyesters structure, whereas their glass transition temperatures (Tg) showed a beneficial increase ranging from 76.8 °C to 103.5 °C. Wide-Angle X-ray Diffractometry (WAXD) patterns revealed that a small portion of isosorbide units are inserted into the crystals of PCHDMF, resulting in increase of the interplanar distances and crystal defects. A banded spherulitic morphology was observed, while coarsening of spherulites and increase in band distance occurred with increasing isosorbide content. Thermogravimetric analysis (TGA) results showed an excellent thermal stability up to 360 °C for all copolymers.

We also recommend Trading Suppliers and Manufacturers of 1,4-Cyclohexanedimethanol (cas 105-08-8). Pls Click Website Link as below: cas 105-08-8 suppliers

Prev:Matrix dependence of the conformations of the 1,4-DIETHYLBENZENE (cas 105-05-5) radical cation at low temperatures
Next:Fibers spun from 1,4-Cyclohexanedimethanol (cas 105-08-8)-modified polyethylene terephthalate resin)