Copper acetylacetonate anchored onto amine-functionalised clays

Add time:08/16/2019    Source:sciencedirect.com

Copper (II) acetylacetonate was immobilised directly onto two clays, laponite (Lap) and K10-montmorillonite (K10), and after their amine functionalisation with (3-aminopropyl)triethoxysilane (APTES). All the materials were characterised by nitrogen adsorption isotherms at −196 °C, elemental analysis, TG-DSC, XRD, and IR spectroscopy. The K10-based materials were also characterised by XPS. The APTES-functionalised K10 showed higher copper loading than K10, indicating that the clay functionalisation enhanced the complex immobilisation; on the contrary, in Lap-based materials higher metal content was obtained by direct complex anchoring, probably due to the delaminated nature of Lap which induced the particles aggregation on functionalisation with APTES. All the results pointed out that the Cu complex was anchored onto the amine-functionalised clays by Schiff condensation between the amine groups of anchored APTES and the carbonyl groups of the acetylacetonate ligand, whereas direct immobilisation proceeded mostly through interaction between the metal centre and the clay surface hydroxyl groups.

We also recommend Trading Suppliers and Manufacturers of POTASSIUM ACETYLACETONATE (cas 19393-11-4). Pls Click Website Link as below: cas 19393-11-4 suppliers

Prev:Thermal stability, sublimation pressures and diffusion coefficients of some metal acetylacetonates
Next:Triazidation of 2,4,6-trifluorobenzenes)