Comparison of source/drain electrodes in thin-film transistors based on room temperature deposited ZINC NITRIDE (cas 1313-49-1) films

Add time:08/15/2019    Source:sciencedirect.com

In this work, the comparison of source/drain electrodes in thin film transistors (TFTs) based on room temperature deposited ZINC NITRIDE (cas 1313-49-1) (Zn3N2) films is presented. Aluminum and aluminum doped zinc oxide (AZO) films are used as electrodes. Both devices exhibit an on/off-current ratio of 104 and a subthreshold slope close to 1 V/Dec. The extracted field-effect mobility was 4.5 cm2/Vs and 1 cm2/Vs for TFTs using aluminum and AZO, respectively. Better electrical characteristics are achieved with aluminum electrodes. However, AZO electrodes made possible the fabrication of fully transparent Zn3N2 TFTs, reported for first time in this work.

We also recommend Trading Suppliers and Manufacturers of ZINC NITRIDE (cas 1313-49-1). Pls Click Website Link as below: cas 1313-49-1 suppliers

Prev:Solvent free clean selective oxidation of alcohols catalyzed by mono transition metal (Co, Mn, Ni)-substituted Keggin-phosphomolybdates using hydrogen peroxide
Next:Highly transparent ZINC NITRIDE (cas 1313-49-1) thin films by RF magnetron sputtering with enhanced optoelectronic behavior)