Enhanced anti-ultraviolet, anti-fouling and anti-bacterial polyelectrolyte membrane of polystyrene grafted with trimethyl quaternary ammonium salt modified lignin

Add time:08/23/2019    Source:sciencedirect.com

A polyelectrolyte membrane with anti-ultraviolet, anti-fouling, and antibacterial abilities was prepared using trimethyl quaternary ammonium salt grafting lignin (QAL) and polystyrene (PS) at different ratios. Contact angle measurements indicated that the addition of QAL into the PS blending membrane altered the hydrophilicity by trimethyl quaternary ammonium groups and phenolic hydroxyl groups of QAL. Furthermore, the phenylpropane structural unit in the lignin formed double bonds by conjugating with carbonyl groups and formed p-π by conjugating with phenolic hydroxyl of side chains. For this reason, the produced composite membranes displayed high potential and commercial importance for absorbing ultraviolet light. The ultraviolet transmission values of all the PS/QAL blending membranes were close to zero ranging from 200 to 400 nm. The QAL5-PS membrane had less variation in the gas transmission rate (−6.388 cm3/m2/day/atm) than that of PS membrane (−32.9 cm3/m2/day/atm) after 5 circles of bovine serum albumin (BSA) fouling. The inhibition zone of the QAL5-PS membrane was 10.4 ± 0.06 mm, and almost zero for the neat PS membrane, indicating a much better antibacterial performance of the QAL-PS composite membranes than that of pure PS membranes.

We also recommend Trading Suppliers and Manufacturers of trimethyl(trimethylamine)aluminium (cas 19553-62-9). Pls Click Website Link as below: cas 19553-62-9 suppliers

Prev:Trimethylamine sensors with enhanced anti-humidity ability fabricated from La0.7Sr0.3FeO3 coated In2O3–SnO2 composite nanofibers
Next:Electrospun nanofibers of p-type NiO/n-type ZnO heterojunction with different NiO content and its influence on trimethylamine sensing properties)