Growth of AlxGa1−xAs by reduced pressure MOVPE using trimethylamine alane
-
Add time:08/28/2019 Source:sciencedirect.com
High quality epitaxial layers of AlxGa1-xAs have been grown by reduced pressure MOVPE using the new aluminium precursor trimethylamine alane in combination with trimethylgallium and arsine. The layers were grown at 650°C and were shown to possess n-type conductivity for all aluminium compositions. Low temperature photoluminescence data indicated that carbon was still present in the low aluminium content layers. In marked contrast to previous studies at atmospheric pressure, the AlGaAs layers grown at low pressure using trimethylamine alane were of high compositional and thickness uniformity.
We also recommend Trading Suppliers and Manufacturers of trimethyl(trimethylamine)aluminium (cas 19553-62-9). Pls Click Website Link as below: cas 19553-62-9 suppliers
Prev:The crystal structure of trimethyl(quinuclidine)aluminum
Next:PMMA-N,N,N-trimethyl chitosan nanoparticles for fabrication of antibacterial natural rubber latex gloves) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Anaerobic growth of halophilic archaeobacteria by reduction of dimethysulfoxide and trimethylamine N-oxide08/30/2019
- PMMA-N,N,N-trimethyl chitosan nanoparticles for fabrication of antibacterial natural rubber latex gloves08/29/2019
- The crystal structure of trimethyl(quinuclidine)aluminum08/27/2019
- Original Research PaperPreparation of aluminum–organic nanocomposite materials via wet chemical process08/26/2019
- The adsorption and thermal decomposition of trimethylamine alane on aluminum and silicon single crystal surfaces: kinetic and mechanistic studies08/25/2019
- Electrospun nanofibers of p-type NiO/n-type ZnO heterojunction with different NiO content and its influence on trimethylamine sensing properties08/24/2019
- Enhanced anti-ultraviolet, anti-fouling and anti-bacterial polyelectrolyte membrane of polystyrene grafted with trimethyl quaternary ammonium salt modified lignin08/23/2019
- Trimethylamine sensors with enhanced anti-humidity ability fabricated from La0.7Sr0.3FeO3 coated In2O3–SnO2 composite nanofibers08/22/2019