The formation of a peroxoantimonate thin film coating on graphene oxide (GO) and the influence of the GO on its transformation to antimony oxides and elemental antimony

Add time:08/27/2019    Source:sciencedirect.com

The ultrathin peroxoantimonate coating of graphene oxide from hydrogen peroxide-rich solutions of hydroxoantimonate is demonstrated. An amorphous 1–2 nm Sb (V) oxide film is formed and can be further crystallized by exposure to an electron beam to give a 2–5 nm thick supported Sb6O13 particulate coating. Heat treatment of the peroxoantimonate yielded different crystalline oxides, whereas in the presence of the graphene support only trigonal Sb (0) was produced by heat treatment in vacuum or an argon atmosphere. The graphene oxide support is essential for the formation of the Sb (0) phase and even in air a substantial elemental antimony was obtained. Whereas heat treatment of uncoated graphene oxide in an inert atmosphere produces reduced graphene oxide, the antimony oxide coated graphene oxide is not reduced by the heat treatment. Only after the supported antimony oxide is reduced to give the trigonal Sb (0) phase the graphene oxide was reduced by the heat treatment. The phases before and after the different heat treatments are characterized by electron and X-ray diffraction, thermal analysis, XPS studies, electron microscopy and wet chemistry.

We also recommend Trading Suppliers and Manufacturers of antimony pentoxide sol (cas 12712-36-6). Pls Click Website Link as below: cas 12712-36-6 suppliers

Prev:Review ArticleElectrochromic properties of sol–gel prepared hybrid transition metal oxides – A short review
Next:Effect of calcination temperatures on physicochemical properties of vanadium–antimony mixed oxide catalysts)