N-doped ZIF-8-derived carbon (NC-ZIF) as an anodic material for lithium-ion batteries

Add time:08/27/2019    Source:sciencedirect.com

Zeolitic Imidazolate Framework-8 (ZIF-8) has attracted great attention from different research fields owing to its high specific surface area and three-dimensional (3D) frameworks. Moreover, ZIF-8 can be converted into nitrogen doping porous carbon material by high temperature calcination. In our report, A N-doped ZIF-8-derived carbon (NC-ZIF) is synthesized at different temperatures as anode material for lithium-ions battery. The NC-ZIF shows regular polyhedral morphology, high specific surface area and porous structure, which providing a fast transportion path, more active sites for lithium-ions and suppressing volume expansion caused by intercalation and deintercalation of lithium-ions. The NC-800 (ZIF-8 annealed at 800 °C) contented 16.2 wt% N and a small amount of ZnO, which exhibits the best lithium storage performance with high capacity and long cycle lifetime. The initial reversible capacity 465.0 mAh∙g−1 is attained, and the capacity remains 440.5 mAh∙g−1 after 100 cycles at a current density of 100 mA∙g−1, with the capacity retention of 94.7%. Even at a high rate of 500 mA∙g−1, the reversible capacity of 211.2 mAh∙g−1 can maintain over 300 cycles with a capacity fading of 0.28% per cycle. Therefore, NC-800 is a very promising anode material for lithium-ion batteries.

We also recommend Trading Suppliers and Manufacturers of N(8)-norphysostigmine (cas 19573-10-5). Pls Click Website Link as below: cas 19573-10-5 suppliers

Prev:A high-efficiency diffusion process in carbonized ZIF-8 incorporated mixed matrix membrane for n-butanol recovery
Next:Research paperThe structure and stability of CrnTem (1 ≤ n ≤ 6, 1 ≤ m ≤ 8) clusters)