The effect of prepolymer crystallinity on solid-state polymerization of poly(bisphenol A carbonate)
-
Add time:09/02/2019 Source:sciencedirect.com
The effect of prepolymer crystallinity on the solid-state polymerization (SSP) of poly(bisphenol A carbonate) was examined using nitrogen as a sweep fluid. A low-molecular-weight prepolymer was synthesized by melt transesterification and prepolymers with different crystallinities (11.7%, 23.3%, 33.7%) were prepared with supercritical carbon dioxide treatment. SSP of the three prepolymers was then carried out at reaction temperatures in the range of 150–190 °C, with a prepolymer particle size of 75 μm and a N2 flow rate of 1600 ml/min. The glass-transition temperature (Tg), absolute weight-average molecular weight (Mn), and percent crystallinity were measured at various times during each SSP. At each reaction temperature, SSP of the lower crystallinity prepolymer (11.7%) always resulted in higher-molecular-weight polymers, compared with the polymers synthesized using the higher crystallinity prepolymer (23.3% and 33.7%). The crystallinity of the polymers synthesized from the high crystallinity prepolymer was significantly higher than for those synthesized from the low crystallinity prepolymer. Higher crystallinity of the prepolymer and the synthesized polymers may lower the reaction rate by reducing chain-end mobility or/and by inhibiting byproduct diffusion.
We also recommend Trading Suppliers and Manufacturers of POLY(BISPHENOL A CARBONATE) (cas 111211-39-3). Pls Click Website Link as below: cas 111211-39-3 suppliers
Prev:Pyrolysis mechanism and thermal degradation kinetics of poly(bisphenol A carbonate)-based polymers originating in waste electric and electronic equipment
Next:Formation of bisphenol A by thermal degradation of poly(bisphenol A carbonate)) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Transesterifications of poly(bisphenol A carbonate) with caprolactone segments in copolyester and poly(ε-caprolactone) homopolymer09/07/2019
- Rare Earth metal triflates M(O3SCF3)3 (M = Sc, Yb, La) as Lewis acid catalysts of depolymerization of poly-(bisphenol A carbonate) via hydrolytic cleavage of carbonate moiety: Catalytic activity of La(O3SCF3)309/06/2019
- Enhanced nonlinear optical properties of octa-substituted lead and cadmium phthalocyanines when embedded in poly(bisphenol A carbonate) as thin films09/05/2019
- Selective cell adhesion on an ion implanted poly(bisphenol A carbonate) film09/04/2019
- Formation of bisphenol A by thermal degradation of poly(bisphenol A carbonate)09/03/2019
- Pyrolysis mechanism and thermal degradation kinetics of poly(bisphenol A carbonate)-based polymers originating in waste electric and electronic equipment09/01/2019
- Integral Recovery of Bisphenol from Poly-Bisphenol A Carbonate via Hydrolysis08/31/2019
- Full length articleFormation of polymer nanoparticles by UV pulsed laser ablation of poly (bisphenol A carbonate) in liquid environment08/30/2019
- Chemical recycling of poly(bisphenol A carbonate): 1,5,7-Triazabicyclo[4.4.0]-dec-5-ene catalyzed alcoholysis for highly efficient bisphenol A and organic carbonate recovery08/29/2019
-
Health and Chemical more >
-
Related Products