Short communicationCrystal structure, infrared spectra and microwave dielectric properties of low-firing La2Zr3(MoO4)9 ceramics prepared by reaction-sintering process

Add time:09/03/2019    Source:sciencedirect.com

Low-firing La2Zr3(MoO4)9 (LZM) ceramics were prepared using the reaction-sintering (RS) route for the first time. The crystal structure, sintering characteristics, microstructure and microwave dielectric properties of LZM samples were explored scientifically. A single phase, with trigonal structure in R-3c space group, was formed at 600–800 °C. Dense sample with high relative density (>92 %) and homogeneous microstructure was obtained at 650 °C. Subsequently, EDS analysis revealed that the composition was corresponding to theoretical stoichiometric ratio of chemical formula. The chemical bonds theory of complex crystals and far-infrared spectra analysis were employed to investigate the structure-property relations of LZM samples in detail. Optimum microwave dielectric properties with a dielectric constant (εr) of 10.17, a quality factor (Q·f) of 51,578 GHz and a temperature coefficient of resonant frequency (τf) of -29.55 ppm/°C were achieved in LZM sample prepared by the RS process sintered at 650 °C.

We also recommend Trading Suppliers and Manufacturers of Red 9 (cas 1342-67-2). Pls Click Website Link as below: cas 1342-67-2 suppliers

Prev:Adsorptive removal of triarylmethane dye (Basic Red 9 (cas 1342-67-2)) from aqueous solution by sepiolite as effective and low-cost adsorbent
Next:A molecularly imprinted polymer-based evanescent wave fiber optic sensor for the detection of basic Red 9 (cas 1342-67-2) dye)