The effect of the local microstructure of MRI 201S magnesium alloy on its corrosion rate
-
Add time:09/03/2019 Source:sciencedirect.com
The corrosion rates of High Density Die Cast MRI 201S and three other magnesium alloys in 3% NaCl were measured.The side surfaces of some specimens were insulated by a polymer, while the other specimens had all the surfaces open to the corrosive media. No difference between the two types of specimens for was observed for AZ91D, MRI 153M and MRI 202S alloys, while for MRI 201S alloy the corrosion of the samples of the 1st type was significantly slower than of the 2nd type. For all the alloys studied, the coarser the grains the higher the corrosion rate.
We also recommend Trading Suppliers and Manufacturers of nitric acid, magnesium neodymium salt (cas 19696-95-8). Pls Click Website Link as below: cas 19696-95-8 suppliers
Prev:On the stability of the oxides film formed on a magnesium alloy containing rare-earth elements
Next:Corrosion behavior, biocompatibility and biomechanical stability of a prototype magnesium-based biodegradable intramedullary nailing system) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Full length articleGadolinium accumulation in organs of Sprague–Dawley® rats after implantation of a biodegradable magnesium-gadolinium alloy09/06/2019
- Synthesis and characterisation of diamide extractants for the extraction of neodymium09/05/2019
- Corrosion behavior, biocompatibility and biomechanical stability of a prototype magnesium-based biodegradable intramedullary nailing system09/04/2019
- On the stability of the oxides film formed on a magnesium alloy containing rare-earth elements09/02/2019
- Hot corrosion behaviour of rare-earth magnesium hexaaluminate based thermal barrier coatings under molten sulphate-vanadate salts09/01/2019
- Effect of the addition of low rare earth elements (lanthanum, neodymium, cerium) on the biodegradation and biocompatibility of magnesium08/31/2019
-
Health and Chemical more >