Synthesis and pyrolysis of silicon and tin containing poly(2,2′-dioxy-1,1′-biphenoxy-phosphazenes)

Add time:09/07/2019    Source:sciencedirect.com

The polyphosphazene {[NP(O2C12H8)]0.5[NP(OC6H4Br)2]0.5}n (1) [(O2C12H8) = 2,2′-dioxy-1,1′-biphenyl] that, as an strictly alternating copolymer, can be considered nearly as the homopolymer [NP(O2C12H8)NP(OC6H4Br)2]n, was reacted first with tBuLi in THF at −78 °C to give the intermediate [NP(O2C12H8)NP(OC6H4Li)2]n (2) and subsequently with the chlorosilanes SiMe3Cl and SiMe2(C6H5)Cl or with the chlorostannane SnMe3Cl, to obtain the new polyphosphazenes {(NP[O2C12H8])0.5[NP(OC6H4SiMe3)2]0.5−x[NP(OC6H5)(OC6H4SiMe3)]x}n (3a) (x = 0.15–0.5), {(NP[O2C12H8])0.5[N(POC6H4SiMe2Ph)2]0.2[NP(OC6H5)(OC6H4SiMe2Ph)]0.3}n (3b), and {(NP[O2C12H8])0.5[NP(OC6H5)(OC6H4SnMe3)]0.5}n (4), having a very regular distribution of the silicon or tin organometallic sites along the chains. The pyrolysis of the polymers in air at 800 °C gave microcrystalline residues (characterized by IR, XRD, SEM and TEM-EDXA) consisting on phases of SiO2 · P2O5 · P2O7.9 · SiP2O7, or, in the case of the tin derivative, almost pure SnP2O7. The results indicate that, while part of the Si content is lost during the pyrolysis, almost all the tin in the original polymer was incorporated to the final residue.

We also recommend Trading Suppliers and Manufacturers of tin diphosphate (cas 18472-93-0). Pls Click Website Link as below: cas 18472-93-0 suppliers

Prev:Synthesis and characterization of alkali-metal tin(II) phosphates: Na10Sn31(HPO4)6(P2O7)6(PO4)12 and K2SnP2O7
Next:A mixed cation nickel diphosphate with a layered intergrowth structure: synthesis, structural and magnetic characterization of Na(NH4)[Ni3(P2O7)2(H2O)2])