Synergetic effects of curing temperature and hydration reactivity of MgO expansive agents on their hydration and expansion behaviours in cement pastes

Add time:09/09/2019    Source:sciencedirect.com

Effects of curing temperature on the hydration and expansion behaviours of MgO expansive agents with different reactivities in cement pastes were investigated via quantitative examination on the hydration degree of MgO, expansion, and microstructure of the cement pastes cured under various temperatures. Results reveal that reactive MgO with a reactivity value of 65 s (represented as MEA-R) produces more rapid and greater expansions than the less reactive MgO with a reactivity value of 145 s (MEA-M) at early age (within 28 d) and less expansions at late age under 20 °C. However, under higher temperatures (20 °C–80 °C) or at late age, the MEA-M produces larger expansions. The curing temperature has a synergetic influence on the hydration and expansion of cement pastes containing MgO expansive agents. MEA-M is more sensitive to the curing temperature as more considerable differences are caused among the expansions of cement pastes cured under different temperatures.

We also recommend Trading Suppliers and Manufacturers of CURING AGENT C (cas 13732-62-2). Pls Click Website Link as below: cas 13732-62-2 suppliers

Prev:Synthesis of an effective bio-based flame-retardant curing agent and its application in epoxy resin: Curing behavior, thermal stability and flame retardancy
Next:A novel liquid imidazole-copper (II) complex as a thermal latent curing agent for epoxy resins)