Latent curing epoxy systems with reduced curing temperature and improved stability

Add time:09/26/2019    Source:sciencedirect.com

As a representative single component epoxy resin, diglycidyl ether of bisphenol A resin (DGEBA) is the most widely used matrix in adhesives. However, challenges are still remained including high curing temperature and short shelf life. Herein, bisphenol A (BPA), Tetrachlorobisphenol A (TCBPA), and Tetrabromobisphenol A (TBBPA) as latent curing agents and imidazole as accelerator were used in adhesives. Curing kinetics was studied by non-isothermal DSC, using a model-fitting Málek approach and a model-free advanced isoconversional method of Vyazovkin. Results indicated that curing temperature of EP-BPA, EP-TCBPA, and EP-TBBPA was reduced to 126 ℃, 94 ℃, and 106 ℃, respectively. Storage stability evaluated by DSC indicated the shelf life was up to five months. After curing, molecular weights of the as-prepared linear polymers (EP-BPA, EP-TCBPA, and EP-TBBPA) were 33,822 g/mol, 14,913 g/mol, and 18,846 g/mol, and their tensile strength and shear strength were more than 40.06 MPa and 13.64 MPa, respectively.

We also recommend Trading Suppliers and Manufacturers of CURING AGENT C (cas 13732-62-2). Pls Click Website Link as below: cas 13732-62-2 suppliers

Prev:Fabrication of low-temperature curing PES coatings with excellent anti-corrosion properties by introducing the crosslinking agent
Next:Perforated cenospheres: A reactive internal curing agent for alkali activated slag mortars)