Surface chemical functionalization of cellulose nanocrystals by 3-Aminopropyltriethoxysilane (cas 919-30-2)
-
Add time:07/12/2019 Source:sciencedirect.com
Surface functionalization of cellulose nanocrystals (CNCs) is valuable option to tailor properties as well as increase opportunities for their application. In this study, the surface of CNCs was functionalized with 3-aminopropyltriethoxysilane (APTES), without using hazardous solvents and by a direct, simple and straightforward method. APTES was firstly hydrolyzed in water and then adsorbed onto CNC through hydrogen bonds, finally the chain hydrocarbon was covalently linked to the surface of CNC through SiOC bonds which formed via the condensation reaction between hydroxyl and silanol groups. The chemical modification of the CNCs surface was confirmed by ATR-IR and NMR spectroscopy. Experiments conducted by AFM and XRD showed no significant change in the CNC dimensions and crystalline structure as a result of the modification. The EDX and XPS results confirmed the exsistence of APTES onto the CNCs. Silylated CNC exhibited good thermal stability and a greater amount of residual char was formed at 500 °C compared to non-chemically modified CNC. Thus, The silylation of CNCs may offer applications in composite manufacturing, where these nanoparticles have limited dispersibility in hydrophobic polymer matrices, and as nano-adsorbers due to the presence of amino groups attached on the surface.
We also recommend Trading Suppliers and Manufacturers of 3-Aminopropyltriethoxysilane (cas 919-30-2). Pls Click Website Link as below: cas 919-30-2 suppliers
Prev:The effect of electro-migrating 3-Aminopropyltriethoxysilane (cas 919-30-2) on the improvement of the reinforced concrete durability
Next:Silylation of TEMPO oxidized nanocellulose from oil palm empty fruit bunch by 3-Aminopropyltriethoxysilane (cas 919-30-2)) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Optimization of graphene-MoS2 barristor by 3-Aminopropyltriethoxysilane (cas 919-30-2) (APTES)07/19/2019
- Functionalization of 4-aminothiophenol and 3-Aminopropyltriethoxysilane (cas 919-30-2) with graphene oxide for potential dye and copper removal07/18/2019
- Effective removal of Cr(VI) from aqueous solution by 3-Aminopropyltriethoxysilane (cas 919-30-2)-functionalized graphene oxide07/17/2019
- Silylation of saponite with 3-Aminopropyltriethoxysilane (cas 919-30-2)07/16/2019
- Preparation and characterization of montmorillonite modified with 3-Aminopropyltriethoxysilane (cas 919-30-2)07/15/2019
- Synthesis of 3-Aminopropyltriethoxysilane (cas 919-30-2)-silica modified polyethersulfone hollow fiber membrane for oil-in-water emulsion separation07/14/2019
- Silylation of TEMPO oxidized nanocellulose from oil palm empty fruit bunch by 3-Aminopropyltriethoxysilane (cas 919-30-2)07/13/2019
- The effect of electro-migrating 3-Aminopropyltriethoxysilane (cas 919-30-2) on the improvement of the reinforced concrete durability07/11/2019