Oxidation protection of aluminum metaphosphate coating prepared by cathodic electrochemical treatment for graphite

Add time:07/18/2019    Source:sciencedirect.com

In order to provide a short-term oxidation protection system for graphite at high temperature, an aluminum metaphosphate coating was prepared on the surface of graphite by cathodic electrochemical treatment, and its oxidation protective ability was investigated using an isothermal oxidation test. The microstructure, chemical composition, and phase components of the aluminum metaphosphate coating were respectively analyzed through scanning electron microscope, dispersive X-ray analysis, and X-ray diffraction. The results showed that aluminum metaphosphate coating with a thickness of about 24 μm provides good oxidation resistance for graphite at 1250 °C, and it reduces the oxidation rate of graphite in a 5-h period by a factor of two. The good oxidation protective ability of the as-prepared coating at 1250 °C is related to the formation of a layer consisting of aluminum metaphosphate and aluminum orthophosphate phases.

We also recommend Trading Suppliers and Manufacturers of ALUMINUM OXIDE (cas 11092-32-3). Pls Click Website Link as below: cas 11092-32-3 suppliers

Prev:Low-temperature laser generated ultrathin ALUMINUM OXIDE (cas 11092-32-3) layers for effective c-Si surface passivation
Next:Synergistic effect of poly(3,4-ethylenedioxythiophene), reduced graphene oxide and aluminium oxide) as counter electrode in dye-sensitized solar cell)