Direct solid state synthesis of W–Al2O3 nanostructured composite using Ammonium paratungstate (cas 11120-25-5) (APT) and Al powder mixture

Add time:07/26/2019    Source:sciencedirect.com

W–Al2O3 nanostructured composite has been produced by mechanical milling of Ammonium paratungstate (cas 11120-25-5) (APT) and Al powder mixture at room temperature. The milled products have been characterized by X-ray diffraction (XRD), and scanning electron microscopy (SEM) equipped with energy dispersive spectrometry (EDS). The XRD and EDS results confirmed that direct reduction of APT to α-W took place after 25 min milling. It was observed that α → β phase transition took place after 24 h mechanical milling. SEM micrographs showed that alumina matrix composite reinforced with W could be obtained by one step MSR (mechanically induced self-propagation reaction) process. X-ray diffraction peak broadening equation confirmed that the mean grain size of these particles was in nanometer range which gradually decreased with increasing the milling time.

We also recommend Trading Suppliers and Manufacturers of Ammonium paratungstate (cas 11120-25-5). Pls Click Website Link as below: cas 11120-25-5 suppliers

Prev:Carburization of Ammonium paratungstate (cas 11120-25-5) by methane: The influence of reaction parameters
Next:A convenient synthesis of carbohydrate derived furo/pyrano[2,3-b]pyrans from 2-hydroxymethyl glycals)