Leaching behavior of impurities in Ca-alloyed metallurgical grade silicon

Add time:07/20/2019    Source:sciencedirect.com

To explore the potential of acid leaching in purifying metallurgical grade silicon (MG-Si) for solar cell applications, the effect of silicon microstructure on its leaching behavior was systematically investigated in the present work by a combination of alloying refining with acid etching. The microstructure evolution of silicon was revealed before and after acid etching with different lixiviants. Calcium-containing precipitates were found in MG-Si after alloying with calcium. The etching results showed that the leaching behavior of impurity inclusions strongly depended on the composition of the major impurities. HCl + HF mixture was an effective lixiviant for dissolving impurity inclusions in both MG-Si and its alloy with calcium. The impurity removal efficiency of acid leaching of MG-Si was efficiently improved after alloying. Moreover, the kinetics of acid leaching of MG-Si after alloying with calcium was further discussed based on cracking shrinking model.

We also recommend Trading Suppliers and Manufacturers of Silicon alloy, base, Si,Ca,Mn (cas 11125-27-2). Pls Click Website Link as below: cas 11125-27-2 suppliers

Prev:Some particularities of the corrosion behaviour of Mg–Zn–Mn–Si–Ca alloys in alkaline chloride solutions
Next:The role of Ca microalloying on the microstructure and corrosion behavior of Mg–6Zn–Mn–(0.5–2)Si alloys)