Hydrophobic coatings for improving corrosion resistance of manganese substrate

Add time:07/24/2019    Source:sciencedirect.com

Herein hydrophobic coatings on the surface of manganese were fabricated by immersing manganese substrate into passivation solution with stearic acid (SA) and stearic acid diethanolamide (SDEA). The novelty is that micelles of SDEA can help insoluble SA largely dissolve in solution, then SA and SDEA form hydrophobic passivation coatings simultaneously to greatly improve corrosion resistance of manganese substrate. The characteristics of passivation coatings (corrosion resistance, surface wettability, surface morphology, density and roughness) and passivation solution (stability, particle size and viscosity) were discussed in detail. The formation mechanism of hydrophobic coatings was explained by the results of FT-IR, XPS and Gaussian simulation. After passivation, the corrosion potential of manganese was shifted from −1.462 to −0.979 V, the corrosion current density was reduced from 3.429E−04 to 2.720E−07 A/cm2.

We also recommend Trading Suppliers and Manufacturers of formic acid, manganese salt (cas 14998-38-0). Pls Click Website Link as below: cas 14998-38-0 suppliers

Prev:Fractional removal of manganese and ammonia nitrogen from electrolytic metal manganese residue leachate using carbonate and struvite precipitation
Next:Apparent availability of zinc, selenium and manganese as inorganic metal salts or organic forms in plant-based diets for Atlantic salmon (Salmo salar))