Improved magnetic and microwave absorption properties of MANGANESE NITRIDE (cas 12033-07-7)s through the addition of ferrous

Add time:07/28/2019    Source:sciencedirect.com

(Mn,Fe)-N series micron particles were gotten by high-energy ball milling and consequent annealing of the ferrous and the manganese nitrides powders with different Fe/Mn-N ratios. The phase structures and the magnetic properties, as well as microwave absorption properties of the milled-annealed particles were studied. It was found that phase structures and saturation magnetization Ms changed with the variation of the Fe/Mn-N ratios. The highest Ms about 20.7emu/g was obtained at Fe/Mn-N ratio of 20%. The complex permittivity and permeability behaviors of the milled-annealed particles have been studied in 1–18 GHz. The reflection loss (RL) value exceeding −10  dB at all match thickness and maximum RL values of −23.7 dB with a matching thickness of 2 mm were obtained on particles at Fe/Mn-N ratio of 5%.

We also recommend Trading Suppliers and Manufacturers of MANGANESE NITRIDE (cas 12033-07-7). Pls Click Website Link as below: cas 12033-07-7 suppliers

Prev:Supercapacitive properties of MANGANESE NITRIDE (cas 12033-07-7) thin film electrodes prepared by reactive magnetron sputtering: Effect of different electrolytes
Next:Influence of alkali metal amides on the catalytic activity of MANGANESE NITRIDE (cas 12033-07-7) for ammonia decomposition)