Damage of magnesium potassium phosphate cement under dry and wet cycles and sulfate attack

Add time:07/17/2019    Source:sciencedirect.com

Magnesium potassium phosphate cement (MKPC) produced by dead burnt magnesia (MgO) and potassium dihydrogen phosphate (KH2PO4) is a rapid repairing material. In order to repair concrete structures under dry-wet cycles and sulfate attack condition, the degradation of MKPC under the dry-wet cycles in 5 wt% Na2SO4 solution was analyzed by investigating the mass loss and compressive strength in this paper. In addition, the influences of fly ash and quartz sand on the MKPC were also discussed. The degradation mechanism of the MKPC samples and influence mechanism of fly ash and quartz sand were analyzed based on the pore structure, XRD and SEM. The mass and compressive strength of MKPC progressively decrease after dry-wet cycles. The pore structure of MKPC was optimized by fly ash; the sample with fly ash showed improved durability under dry-wet cycles. The sample with quartz sand showed poor durability under dry-wet cycles since the quartz sand led to the initial defect and interfacial transition zone in the MKPC matrix.

We also recommend Trading Suppliers and Manufacturers of POTASSIUM AMMONIUM SULFATE (cas 23208-79-9). Pls Click Website Link as below: cas 23208-79-9 suppliers

Prev:Raman Study of Sodium Potassium Sulphate Crystals
Next:High time-resolved measurements of water-soluble sulfate, nitrate and ammonium in PM2.5 and their precursor gases over the Eastern Mediterranean)