The ability of silicide coating to delay the catastrophic oxidation of vanadium under severe conditions

Add time:07/31/2019    Source:sciencedirect.com

V–4Cr–4Ti vanadium alloy is a potential cladding material for sodium-cooled fast-neutron reactors (SFRs). However, its affinity for oxygen and the subsequent embrittlement that oxygen induces causes a need for an oxygen diffusion barrier, which can be obtained by manufacturing a multi-layered silicide coating. The present work aims to evaluate the effects of thermal cycling (using a cyclic oxidation device) and tensile and compressive stresses (using the three-point flexure test) on the coated alloy system. Tests were performed in air up to 1100 °C, which is 200 °C higher than the accidental temperature for SFR applications. The results showed that the VSi2 coating was able to protect the vanadium substrate from oxidation for more than 400 1-h cycles between 1100 °C and room temperature. The severe bending applied to the coated alloy at 950 °C using a load of 75 MPa did not lead to specimen breakage. It can be suggested that the VSi2 coating has mechanical properties compatible with the V–4Cr–4Ti alloy for SFR applications.

We also recommend Trading Suppliers and Manufacturers of VANADIUM SILICIDE (cas 12039-76-8). Pls Click Website Link as below: cas 12039-76-8 suppliers

Prev:Low-energy Ar+ ion-beam induced VANADIUM SILICIDE (cas 12039-76-8) formation at V/Si interfaces
Next:Elastic properties and electronic structure of VANADIUM SILICIDE (cas 12039-76-8)s-a density functional investigation)