Formation of VANADIUM SILICIDE (cas 12039-76-8) by high dose ion implantation

Add time:08/05/2019    Source:sciencedirect.com

The VANADIUM SILICIDE (cas 12039-76-8) system has been found to be of increasing interest because one of the silicide phases viz. V3Si with the A-15 structure is often accompanied by a high temperature superconductivity. We have studied the formation of vanadium silicide layers by high dose ion implantation. 30 keV 51V+ ions were implanted at room temperature onto thermally evaporated a-Si films on thermally grown SiO2 substrates. The samples were annealed in vacuum to study the possible evolution of V-Si phases. Both Seeman-Bohlin X-ray diffraction and Auger/sputter profiling techniques were used to analyse these samples. The observed Auger depth profile of the annealed samples shows a more uniform vanadium distribution as compared to the vanadium distribution in as-implanted samples, along with the changes in the Si L2,3VV lineshape. The X-ray diffraction results show the formation of V3Si, V5Si3 and VSi2 phases. After annealing the sample in vacuum, a more ordered growth of V3Si phase is found to be accompanied by an increase in VSi2 phase. This has been related to the possible changes ocurring in the a-Si layers due to annealing of the sample.

We also recommend Trading Suppliers and Manufacturers of VANADIUM SILICIDE (cas 12039-76-8). Pls Click Website Link as below: cas 12039-76-8 suppliers

Prev:The ohmic contact to the silicon Schottky barrier using VANADIUM SILICIDE (cas 12039-76-8) and gold or silver metallization
Next:Photoluminescent properties of porous films of TANTALUM SILICIDE (cas 12039-79-1)s)