Densification kinetics and mechanical properties of Tantalum carbide (cas 12070-06-3)
-
Add time:08/02/2019 Source:sciencedirect.com
Sintering kinetics and densification of tantalum carbide (TaC) based ultra-high temperature ceramics (UHTC) processed using spark plasma sintering (SPS) were investigated. Samples sintered in the temperature ranging from 1600 °C to 2300 °C for 15 min under uniaxial pressure of 50 MPa showed increasing densification (~77% to 99% from 1600 °C to 2300 °C) accompanied by substantial grain growth (~0.57 μm to ~4.05 μm). Below 1900 °C, the densification mechanism was grain-boundary sliding with an apparent activation energy of 97.3 ± 10.2 kJ/mol. However above 1900 °C, the activation energy was found to be 232.7 ± 19.6 kJ/mol with grain boundary diffusion to be an active densification mechanism. The flexural strength (from 161.3 ± 10.4 MPa to 326.5 ± 10.5 MPa) and elastic modulus (from 375.7 ± 3.1 GPa 535.4 ± 4.7 GPa) was observed to increase with the increasing sintering temperature. The study explicitly establishes that the dense bulk TaC ceramic can be produced by SPS in a shorter time and lower sintering temperature, while maintaining the compositional stoichiometry.
We also recommend Trading Suppliers and Manufacturers of Tantalum carbide (cas 12070-06-3). Pls Click Website Link as below: cas 12070-06-3 suppliers
Prev:Synthesis of ultra-fine Tantalum carbide (cas 12070-06-3) powders by a combinational method of sol–gel and spark plasma sintering
Next:Study of the cell responses in Tantalum carbide (cas 12070-06-3) nanoparticles-enriched polysaccharide composite hydrogel) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Epitaxial growth of Tantalum carbide (cas 12070-06-3)s by low carbon flow carburizing08/04/2019
- Study of the cell responses in Tantalum carbide (cas 12070-06-3) nanoparticles-enriched polysaccharide composite hydrogel08/03/2019
- Synthesis of ultra-fine Tantalum carbide (cas 12070-06-3) powders by a combinational method of sol–gel and spark plasma sintering08/01/2019
- Experimental investigation into the crack propagation in multiphase Tantalum carbide (cas 12070-06-3) ceramics07/31/2019
- Low-temperature synthesis of Tantalum carbide (cas 12070-06-3) by facile one-pot reaction07/30/2019
- Synthesis of Tantalum carbide (cas 12070-06-3) from multiwall carbon nanotubes in a molten salt medium07/29/2019
- Tribological performance of polycrystalline tantalum-carbide-incorporated diamond films on silicon substrates07/28/2019
-
Health and Chemical more >