Manganese in silicon carbide

Add time:08/01/2019    Source:sciencedirect.com

Structural disorder and relocation of implanted Mn in semi-insulating 4H–SiC has been studied. Subsequent heat treatment of Mn implanted samples has been performed in the temperature range 1400–2000 °C. The depth distribution of manganese is recorded by secondary ion mass spectrometry. Rutherford backscattering spectrometry has been employed for characterization of crystal disorder. Ocular inspection of color changes of heat-treated samples indicates that a large portion of the damage has been annealed. However, Rutherford backscattering shows that after heat treatment, most disorder from the implantation remains. Less disorder is observed in the [0 0 0 1] channel direction compared to [112¯3] channel direction. A substantial rearrangement of manganese is observed in the implanted region. No pronounced manganese diffusion deeper into the sample is recorded.

We also recommend Trading Suppliers and Manufacturers of MANGANESE CARBIDE (cas 12121-90-3). Pls Click Website Link as below: cas 12121-90-3 suppliers

Prev:Elucidating the role of κ-carbides in FeMnAlC alloys on abrasion wear
Next:Influence of Ni/Cu ratio in nickel copper carbonate hydroxide on the phase and electrochemical properties)