Water vapor corrosion behavior of lutetium silicates at high temperature

Add time:08/02/2019    Source:sciencedirect.com

The corrosion behavior of hot-pressed lutetium disilicate (Lu2Si2O7) bulk sample in static state water vapor environment was examined at 1300 °C. The apparent corrosion rate was estimated as 1.427 × 10−6 g/cm2 h. The X-ray diffraction pattern showed a trace of Lu2O3 phase on the sample surface after corrosion test. SEM observation on the surface of the sample after corrosion test revealed that the surface morphology was not homogeneous but showing three different types of features. During high-temperature water vapor corrosion, lutetia-rich component first melted, and then removed from the grain surface by water vapor attack. Later, the excess boundary silica phase was removed by water vapor corrosion. These underlying corrosion mechanisms of bulk lutetium disilicate sample in static state water vapor environment were discussed in detail.

We also recommend Trading Suppliers and Manufacturers of LUTETIUM NITRIDE (cas 12125-25-6). Pls Click Website Link as below: cas 12125-25-6 suppliers

Prev:Adsorption, intercalation and sensing of helium on yttrium functionalized open edge boron nitride: A first principle DFT and TDDFT study
Next:High temperature strength of silicon carbide sintered with 1 wt.% aluminum nitride and lutetium oxide)