Non-cavitation tensile creep in Lu-doped silicon nitride

Add time:08/06/2019    Source:sciencedirect.com

The tensile creep behavior of a Lu-doped silicon nitride was studied in the temperature range 1400–1550 °C with test periods of up to 10 200 h. Strain rates were 3–4 orders of magnitude less than those for Yb-doped grades of silicon nitride under the same conditions, suggesting a potential for prolonged operation of this material at temperatures up to 1470 °C. The stress exponent, n, and the activation energy, Q, for creep are 5.3±2.0 and (757±117) kJ/mol, respectively. Precise density and ultra-small-angle X-ray scattering measurements revealed that, in contrast to other grades of silicon nitride, cavitation could not be detected in the material studied. Redistribution of the secondary phases via solution-precipitation combined with grain boundary sliding is discussed as a possible creep mechanism. A discussion of the effect of Lu on viscosity indicates that replacement of Y by Lu may explain the improvement of creep behavior.

We also recommend Trading Suppliers and Manufacturers of LUTETIUM NITRIDE (cas 12125-25-6). Pls Click Website Link as below: cas 12125-25-6 suppliers

Prev:Joining and interface characterization of in situ reinforced silicon nitride
Next:Synthesis and characterization of amorphous MAGNESIUM CARBONATE (cas 12125-28-9) nanoparticles)