Investigation of deep level defects in electron irradiated INDIUM ARSENIDE (cas 1303-11-3) quantum dots embedded in a gallium arsenide matrix

Add time:08/15/2019    Source:sciencedirect.com

Gallium arsenide diodes with and without INDIUM ARSENIDE (cas 1303-11-3) quantum dots were electron irradiated to investigate radiation induced defects. Baseline and quantum dot gallium arsenide pn-junction diodes were characterized by capacitance–voltage measurements, and deep level transient spectroscopy. Carrier accumulation was observed in the gallium arsenide quantum dot sample at the designed depth for the quantum dots via capacitance–voltage measurements. Prior to irradiation, a defect 0.84 eV below the conduction band (EC – 0.84 eV) was observed in the baseline sample which is consistent with the native EL2 defect seen in gallium arsenide. After 1 MeV electron irradiation three new defects were observed in the baseline sample, labeled as E3 (EC – 0.25 eV), E4 (EC – 0.55 eV), and E5 (EC – 0.76 eV), consistent with literature reports of electron irradiated gallium arsenide. Prior to irradiation, the addition of quantum dots appeared to have introduced defect levels at EC – 0.21, EC – 0.38, and EC – 0.75 eV denoted as QD–DX1, QD–DX2, and QD–EL2 respectively. In the quantum dot sample after 1 MeV electron irradiation, QD–E3 (EC – 0.28 eV), QD–E4 (EC – 0.49 eV), and QD–EL2 (EC – 0.72 eV) defects, similar to the baseline sample, were observed, although the trap density was dissimilar to that of the baseline sample. The quantum dot sample showed a higher density of the QD–E4 defect and a lower density of QD–E3, while the QD–EL2 defect seemed to be unaffected by electron irradiation. These findings suggest that the quantum dot sample may be more radiation tolerant to the E3 defect as compared to the baseline sample.

We also recommend Trading Suppliers and Manufacturers of INDIUM ARSENIDE (cas 1303-11-3). Pls Click Website Link as below: cas 1303-11-3 suppliers

Prev:Ternary arsenides based on platinum–indium and palladium–indium fragments of the Cu3Au-type: Crystal structures and chemical bonding
Next:Structural features of indium antimonide quantum dots on the INDIUM ARSENIDE (cas 1303-11-3) substrate)