Full length articleStudies on electrochemical reversibility of LITHIUM TUNGSTATE (cas 13568-45-1) coated Ni-rich LiNi0.8Co0.1Mn0.1O2 cathode material under high cut-off voltage cycling

Add time:08/13/2019    Source:sciencedirect.com

In order to enhance the storage performance and electrochemical reversibility of the Ni-rich LiNi0.8Co0.1Mn0.1O2 cathode material at high cut-off voltage (4.6 V), the surface coating layer of LITHIUM TUNGSTATE (cas 13568-45-1) (Li2WO4) is successfully prepared via a one-step synthesis way followed with a high temperature calcination method. After 500 cycles at 2C in 2.8–4.6 V, the capacity retention of the modified material is improved from 26.95% to 60.62%, and the average discharge voltage can remain at 3.62 V, which is 0.32 V higher than that of the original sample. In addition, after stored in air for 60 days, the discharge capacity of the modified sample still maintains 146 mA h g−1 after 100 cycles at 1C, which has 36% increase than that of the pristine sample. These results are attributed to the fact that the Li2WO4 coating can reduce the interfacial polarization, and enhance Li-ion diffusion and surface stability by suppressing the decomposition of electrolyte on cathode materials with high oxidation surface at high cut-off voltage (4.6 V).

We also recommend Trading Suppliers and Manufacturers of LITHIUM TUNGSTATE (cas 13568-45-1). Pls Click Website Link as below: cas 13568-45-1 suppliers

Prev:A molybdate-incorporated cooperative catalyst: High efficiency in the assisted tandem catalytic synthesis of cyclic carbonates from CO2 and olefins
Next:Original research articleCrystal structure and luminescent properties of two lithium lanthanide tungstate LiLn(WO4)2 (Ln = Sm, Eu))