Evaluation of the influence of experimental parameters in the formation of a vinyltrimethoxysilane (cas 2768-02-7) film on 1010 carbon steel through electrochemical impedance spectroscopy and contact angle techniques
-
Add time:07/17/2019 Source:sciencedirect.com
The influence of experimental parameters on the formation of vinyltrimethoxysilane (cas 2768-02-7) (VTMOS) film to protect 1010 carbon steel against corrosion by electrochemical impedance spectroscopy (EIS) and contact angle measurements was evaluated. Specimens were developed from three 23 factorial designs and an uncoated sample, where the EIS and contact angle were regarded as response variables. The results of coated samples were satisfactory as compared to those of uncoated carbon steel, as the former were better protected against corrosion, besides being more hydrophobic. The optimized specimens showed considerably increased EIS and contact angle values. It is concluded that the design of experiments developed favors to obtain a best finish of VTMOS silane on 1010 carbon steel, according to the EIS and contact angle techniques.
We also recommend Trading Suppliers and Manufacturers of vinyltrimethoxysilane (cas 2768-02-7). Pls Click Website Link as below: cas 2768-02-7 suppliers
Prev:Modification of silicalite-1 by vinyltrimethoxysilane (cas 2768-02-7) (VTMS) and preparation of silicalite-1 filled polydimethylsiloxane (PDMS) hybrid pervaporation membranes
Next:Creation of coating surfaces possessing superhydrophobic and superoleophobic characteristics with fluoroalkyl end-capped vinyltrimethoxysilane (cas 2768-02-7) oligomeric nanocomposites having biphenylene segments) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- An assessment of the corrosion protection of AA2024-T3 treated with vinyltrimethoxysilane (cas 2768-02-7)/(3-glycidyloxypropyl)trimethoxysilane07/21/2019
- Photofunctional binary and ternary Eu3+/Tb3+ hybrid materials with copolymer linkage methacrylic acid–vinyltrimethoxysilane (cas 2768-02-7) and 1,10-phenanthroline07/19/2019
- Creation of coating surfaces possessing superhydrophobic and superoleophobic characteristics with fluoroalkyl end-capped vinyltrimethoxysilane (cas 2768-02-7) oligomeric nanocomposites having biphenylene segments07/18/2019
- Modification of silicalite-1 by vinyltrimethoxysilane (cas 2768-02-7) (VTMS) and preparation of silicalite-1 filled polydimethylsiloxane (PDMS) hybrid pervaporation membranes07/16/2019
- Surface modification of ammonium polyphosphate with vinyltrimethoxysilane (cas 2768-02-7): Preparation, characterization, and its flame retardancy in polypropylene07/15/2019
- Holographic polymer dispersed liquid crystals using vinyltrimethoxysilane (cas 2768-02-7)07/14/2019
- vinyltrimethoxysilane (cas 2768-02-7)-modified zinc oxide quantum dots with tuned optical properties07/13/2019
- Synthesis and Characterization of vinyltrimethoxysilane (cas 2768-02-7)-Grafted Non-Swelling Clay07/12/2019
- Selective modification of kaolinite with vinyltrimethoxysilane (cas 2768-02-7) for stabilization of Pickering emulsions07/11/2019