Efficient supercapattery behavior of mesoporous hydrous and anhydrous cobalt molybdate (cas 14259-85-9) nanostructures
-
Add time:07/16/2019 Source:sciencedirect.com
Hydrous forms of cobalt molybdate (cas 14259-85-9) binary metal oxide nanoaggregates were synthesized via a simple chemical co-precipitation technique. The subsequent heat treatment at 400 °C converted the sample into anhydrous cobalt molybdate (CoMoO4) with mesoporous nanostructure. The anhydrous cobalt molybdate possess surface area and pore volume of 63.92 m2g-1 and 0.1802 cm3g-1 which is much higher than the hydrous cobalt molybdate (1.215 m2g-1 and 0.0072 cm3 g−1). The electrodes designed using these materials exhibited a battery-like behavior with maximum specific capacity of 97 Cg-1 and 177 Cg-1 for hydrous and anhydrous cobalt molybdate samples respectively. In addition, a supercapattery was fabricated utilizing anhydrous cobalt molybdate//activated carbon electrodes, which showed maximum specific capacity value of 64 Cg-1 at 1 Ag-1 discharge specific current and showed better specific energy ∼18.89 Whkg−1 for a specific power of 1.06 kWkg−1. Moreover, the supercapattery exhibited good capacity retention ∼93% after 5000 charge/discharge cycles.
We also recommend Trading Suppliers and Manufacturers of molybdate (cas 14259-85-9). Pls Click Website Link as below: cas 14259-85-9 suppliers
Prev:DIDYMIN (cas 14259-47-3) induces apoptosis through mitochondrial dysfunction and up-regulation of RKIP in human hepatoma cells
Next:High performance of electrocatalytic oxidation in direct glucose fuel cell using molybdate (cas 14259-85-9) nanostructures synthesized by microwave-assisted method) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Iron-doping as an effective strategy to enhance supercapacitive properties of nickel molybdate (cas 14259-85-9)07/25/2019
- Influence of solution pH on forming silver molybdate (cas 14259-85-9)s obtained by sonochemical method and its application for methylene blue degradation07/24/2019
- Eu3+ activated molybdate (cas 14259-85-9)s – Structure property relations07/23/2019
- Leaching kinetics of calcium molybdate (cas 14259-85-9) with hydrochloric acid in presence of phosphoric acid07/22/2019
- Nucleation and morphology of sodium molybdate (cas 14259-85-9) dihydrate from NaOH solution07/20/2019
- molybdate (cas 14259-85-9)-phosphate conversion coatings to protect steel in a simulated concrete pore solution07/21/2019
- Improvement of the corrosion protection of polypyrrole coating for CT3 mild steel with 10-camphorsulfonic acid and molybdate (cas 14259-85-9) as inhibitor dopants07/19/2019
- Water activities of sodium molybdate (cas 14259-85-9) solutions at different temperatures07/18/2019
- High performance of electrocatalytic oxidation in direct glucose fuel cell using molybdate (cas 14259-85-9) nanostructures synthesized by microwave-assisted method07/17/2019