Leaching kinetics of calcium molybdate (cas 14259-85-9) with hydrochloric acid in presence of phosphoric acid
-
Add time:07/22/2019 Source:sciencedirect.com
Calcium molybdate (cas 14259-85-9) (CaMoO4) is the main component of powellite and is a predominant intermediate in the pyrometallurgical and hydrometallurgical process of molybdenum. The extraction of Mo from CaMoO4 by a combination of phosphoric acid and hydrochloric acid was investigated. For further understanding of the leaching mechanism, the effects of five key factors were studied to describe the leaching kinetics. The results indicated that the dissolution rate of CaMoO4 was independent of the stirring speed. Mo extraction significantly increased with increasing HCl concentration and temperature, but decreased with increasing particle size. A shrinking core model with surface chemical reaction was found to withstand the dissolution of CaMoO4. The apparent activation energy was calculated to be 70.879 kJ/mol, and a semi-empirical equation was derived for the rate of reaction.
We also recommend Trading Suppliers and Manufacturers of molybdate (cas 14259-85-9). Pls Click Website Link as below: cas 14259-85-9 suppliers
Prev:Nucleation and morphology of sodium molybdate (cas 14259-85-9) dihydrate from NaOH solution
Next:Eu3+ activated molybdate (cas 14259-85-9)s – Structure property relations) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Iron-doping as an effective strategy to enhance supercapacitive properties of nickel molybdate (cas 14259-85-9)07/25/2019
- Influence of solution pH on forming silver molybdate (cas 14259-85-9)s obtained by sonochemical method and its application for methylene blue degradation07/24/2019
- Eu3+ activated molybdate (cas 14259-85-9)s – Structure property relations07/23/2019
- Nucleation and morphology of sodium molybdate (cas 14259-85-9) dihydrate from NaOH solution07/20/2019
- molybdate (cas 14259-85-9)-phosphate conversion coatings to protect steel in a simulated concrete pore solution07/21/2019
- Improvement of the corrosion protection of polypyrrole coating for CT3 mild steel with 10-camphorsulfonic acid and molybdate (cas 14259-85-9) as inhibitor dopants07/19/2019
- Water activities of sodium molybdate (cas 14259-85-9) solutions at different temperatures07/18/2019
- High performance of electrocatalytic oxidation in direct glucose fuel cell using molybdate (cas 14259-85-9) nanostructures synthesized by microwave-assisted method07/17/2019
- Efficient supercapattery behavior of mesoporous hydrous and anhydrous cobalt molybdate (cas 14259-85-9) nanostructures07/16/2019