Catalysis of nickel acetylacetonate in thermal cure and ceramization of SiC preceramic resin
-
Add time:07/24/2019 Source:sciencedirect.com
In this paper, the efficiency of catalysis of nickel acetylacetonate in the thermal cure and ceramization of a new liquid polymeric precursor (methyl-terminated vinyl-containing oligomethylsilane, PSI) of SiC was investigated. The new liquid PSI was prepared by Wurtz condensation method using lithium as reductant. Under nitrogen atmosphere, the thermal cure was preformed through the mechanism of hydrosilylation, dehydrogen and vinyl polymerization; with the addition of Ni(acac)2 or Co(acac)3 as catalyst, the cure reaction was promoted to proceed at credibly decreased temperature, especially when using Ni(acac)2 as catalyst. With the increase of Ni(acac)2 amount, the thermal curing exotherm of PSI precursor shifted to lower temperatures gradually. Upon pyrolysis, the ceramic yield of PSI precursor was highly improved by catalysis of Ni(acac)2. With the increase of Ni(acac)2 amount, the ceramic yield of PSI precursor was highly increased from 53% to 77%; the growth of crystalline phase was accelerated at the same time. The elements in the pyrolyzed β-SiC were observed to distribute uniformly at micro-scale. The results showed that the catalyst Ni(acac)2 could accelerate thermal cure, promote ceramic crystallization and improve the SiC ceramic yield of PSI precursor.
We also recommend Trading Suppliers and Manufacturers of LITHIUM ACETYLACETONATE (cas 18115-70-3). Pls Click Website Link as below: cas 18115-70-3 suppliers
Prev:One-step solvothermal synthesis of V2O3@C nanoparticles as anode materials for lithium-ion battery
Next:Solvents and supporting electrolytes for vanadium acetylacetonate flow batteries) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Solvents and supporting electrolytes for vanadium acetylacetonate flow batteries07/25/2019
- One-step solvothermal synthesis of V2O3@C nanoparticles as anode materials for lithium-ion battery07/23/2019
- Monodisperse CoFe2O4 nanoparticles supported on Vulcan XC-72: High performance electrode materials for lithium-air and lithium-ion batteries07/22/2019
- Synthesis of carbonaceous/carbon-free nanofibers consisted of Co3V2O8 nanocrystals for lithium-ion battery anode with ultralong cycle life07/20/2019
- Controlled synthesis of nickel carbide nanoparticles and their application in lithium storage07/21/2019
- Reducing hysteresis and enhancing performance of perovskite solar cells using acetylacetonate modified TiO2 nanoparticles as electron transport layers07/19/2019
- Facile synthesis of metal disulfides nanoparticles encapsulated by amorphous carbon composites as high-performance electrode materials for lithium storage07/18/2019
- Measurement and correlation of binary diffusion coefficients of LITHIUM ACETYLACETONATE (cas 18115-70-3) in supercritical carbon dioxide and in liquid ethanol07/17/2019
- Bonding in alkali and alkaline earth acetylacetonates07/16/2019
-
Health and Chemical more >