Preparation and characterization of flame retardant and proton conducting BORON PHOSPHATE (cas 13308-51-5)/polyimide composites

Add time:07/25/2019    Source:sciencedirect.com

In this study novel flame retardant boron phosphate (BPO4)/polyimide composites were prepared. 4,4′-Oxydianiline (ODA) was reacted with 3,3′,4,4′-benzophenonetetracarboxylic dianhydride (BTDA) in dimethyl formamide (DMF) and mixed with BPO4 particles to obtain a series of polyamic acids, meanwhile, corresponding polyimides were synthesized via the thermal imidization technique. The amount of BPO4 in the composite films was varied from 0 wt% to 10 wt%. The structure, thermal and surface properties of the polyimide films were characterized by means of ATR-FTIR, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA) and scanning electron microscopy (SEM). The flame retardancy of the composite materials was examined by limiting oxygen index (LOI) measurements and UL-94 VTM tests. Result showed that the LOI values of composites increased from 28 to 39. Furthermore, proton conductivity of polyimide films was measured by the four probe technique. The composite membrane containing 3 wt% of BPO4 showed a conductivity of 0.4 mS/cm at room temperature.

We also recommend Trading Suppliers and Manufacturers of BORON PHOSPHATE (cas 13308-51-5). Pls Click Website Link as below: cas 13308-51-5 suppliers

Prev:Synthesis, characterization and fuel cell performance tests of boric acid and BORON PHOSPHATE (cas 13308-51-5) doped, sulphonated and phosphonated poly(vinyl alcohol) based composite membranes
Next:Humidity sensing properties of BORON PHOSPHATE (cas 13308-51-5))