Comparing fine particulate Iron hydroxide (cas 11113-66-9) adsorbents for the removal of phosphate in a hybrid adsorption/ultrafiltration system
-
Add time:07/19/2019 Source:sciencedirect.com
The use of micro-sized Iron hydroxide (cas 11113-66-9) adsorbents in mixed reactors is a promising technique for the removal of inorganic contaminants from wastewater within minutes of contact time. This study focusses on phosphate adsorption onto fine fraction granular ferric hydroxide (µGFH) and iron oxy(hydr)oxide agglomerates (IOAs) in a reactor with submerged ultrafiltration (UF) membrane. The performance of the hybrid adsorption/UF membrane system was evaluated for various adsorbents and phosphate concentrations, residence times and concentrations of co-existing ions. The membrane was not fouled at the experimental conditions used (up to 6.3 g/L adsorbent).Phosphate loadings of 20 and 60 mg P/g Fe (36.1 and 108.3 mol P/mol Fe) were reached for µGFH and IOAs, respectively (C0(P) = 4.5 mg/L, deionized water at pH 8, C(Fe) = 0.6 g/L). A shortened residence time of 15 min in the reactor led to a decrease in final loading of 6 mg/g compared to 30 min residence time (54 mg/g compared to 60 mg/g). An extension to 60 min did not result in higher loadings. An increase in adsorbent (IOA) concentration from 0.1 to 0.3 mg/L resulted in an increase of phosphate removal (27 to 35%). Simultaneously, loadings decreased from 50 to 35 mg/g. The application of the developed process for the treatment of artificial secondary effluent resulted in an increase of 87 and 60% in treated volumes until breakthrough (50%) for µGFH and IOAs, respectively, compared to deionized water. Thus, the combined process of adsorption and particle separation using a submerged membrane can be well adjusted according to water composition, initial pollutant concentrations and desired removals.
We also recommend Trading Suppliers and Manufacturers of Iron hydroxide (cas 11113-66-9). Pls Click Website Link as below: cas 11113-66-9 suppliers
Prev:Enhanced adsorptive removal of hydrogen sulfide from gas stream with zinc-Iron hydroxide (cas 11113-66-9) at room temperature
Next:High valence chromium regulated cobalt-iron-hydroxide for enhanced water oxidation) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Partially sulfurated ultrathin nickel-iron carbonate hydroxides nanosheet boosting the oxygen evolution reaction07/23/2019
- Development and regeneration of composite of cationic gel and Iron hydroxide (cas 11113-66-9) for adsorbing arsenic from ground water07/22/2019
- A systematic study of the Iron hydroxide (cas 11113-66-9)-based adsorbent for removal of hydrogen sulphide from biogas07/20/2019
- High valence chromium regulated cobalt-iron-hydroxide for enhanced water oxidation07/21/2019
- Enhanced adsorptive removal of hydrogen sulfide from gas stream with zinc-Iron hydroxide (cas 11113-66-9) at room temperature07/18/2019
-
Health and Chemical more >