Propene Oxidation over Cu2O Single-Crystal Surfaces: A Surface Science Study of Propene Activation at 1 atm and 300 K

Article abstract of DOI:10.1006/jcat.1993.1290

Propene oxidation was studied on Cu2O single-crystal surfaces using XPS and TDS in ultrahigh vacuum (UHV) following propene exposures at 300 K and atmospheric pressure.Three different Cu2O surfaces were examined: a Cu⁺ -terminated (100) surface, an oxygen-terminated (100) surface and a (111) surface with accessible copper cations and lattice oxygen.Selective oxidation to acrolein is promoted by coordinately unsaturated surface lattice oxygen.No clear correlation between the formation of partial oxidation products and oxygen coordination is observed.Both selective and nonselective oxidation products was formed from lattice oxygen.The propene oxidation pathway proceeds through an allyloxy (CH2=CHCH2O-) species where oxygen insertion occurs prior to the second hydrogen abstraction over Cu2O.This conclusion was reached by comparing the propene TDS results from atmospheric pressure exposures with UHV allyl alcohol and acrolein thermal desorption data.The selective oxidation process over Cu2O is subject to a "pressure gap" at 300 K with oxygen insertion occuring at higher pressures, presumably because of translational and collisional activation.However, the subsequent steps in the selective oxidation pathway can be effectively modeled by dissociative adsorption of oxygenates under UHV to stimulate the oxygenated surface intermediates.