Bridgman growth and luminescence properties of dysprosium doped lead potassium niobate crystal

Add time:07/31/2019    Source:sciencedirect.com

Dy-doped lead potassium niobate (Pb2KNb5O15, PKN) single crystal was grown by the modified vertical Bridgman method through spontaneous nucleation. The crystal was brownish, transparent and inclusion free. Five excitation peaks of Dy3+ ions were clearly seen from near ultraviolet region to blue range. It was unique that the excitation peaks in blue range were more intense, especially the one centered at 455 nm. The emission bands consisted of blue, yellow and red emissions, which were at about 487 nm, 573 nm and 662 nm respectively. The CIE chromaticity diagram of PKN:Dy indicated that white light and yellow light could be emitted when the crystal was excited under near ultraviolet light and blue light, respectively. Thus PKN:Dy crystal is a candidate material whose emitting light could be tunable through changing the excited light wavelength.

We also recommend Trading Suppliers and Manufacturers of LEAD NIOBATE (cas 12034-88-7). Pls Click Website Link as below: cas 12034-88-7 suppliers

Prev:Investigation of structure, dielectric and energy-storage properties of lead-free niobate glass and glass-ceramics
Next:High-performance potassium-sodium niobate lead-free piezoelectric ceramics based on polymorphic phase boundary and crystallographic texture)