Effect of impurities introduced by ball milling on hot pressed Boron carbide (cas 12069-32-8)
-
Add time:07/29/2019 Source:sciencedirect.com
Ball milling is commonly used refining process to improve sintering properties of boron carbide. However, this process often leads to the introduction of trace metal impurities into raw materials. It was found in this study that, with prolonged holding time and increased sintering temperature at 2000 °C, these metal impurities led to the recrystallization of boron carbide grains, which significantly affected mechanical properties of sintered boron carbide. Results showed that relative density of sample increased from 98.4%–98.9%, when sintering temperature was raised from 2000 °C to 2050 °C and holding time was extended from 30 min to 60 min. However, under these conditions, flexural strength of boron carbide decreased sharply from 403 MPa to 98 MPa and fracture toughness decreased from 4.4 MPa m1/2 to 2.3 MPa m1/2.
We also recommend Trading Suppliers and Manufacturers of Boron carbide (cas 12069-32-8). Pls Click Website Link as below: cas 12069-32-8 suppliers
Prev:Properties of Boron carbide (cas 12069-32-8) ceramics made by various methods for use in ITER
Next:Preparation of submicron Boron carbide (cas 12069-32-8) powder through gas-solid reaction method) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Does grain size have an influence on intrinsic mechanical properties and conduction mechanism of near fully-dense Boron carbide (cas 12069-32-8) ceramics?08/06/2019
- Structure and mechanical properties of boron-rich Boron carbide (cas 12069-32-8)s08/05/2019
- In-situ synthesis and densification of Boron carbide (cas 12069-32-8) and Boron carbide (cas 12069-32-8)-graphene nanoplatelet composite by reactive spark plasma sintering08/04/2019
- Aluminium 6082-Boron carbide (cas 12069-32-8) composite materials preparation and investigate mechanical-electrical properties with CNC turning08/03/2019
- In situ TEM observations of ion irradiation damage in Boron carbide (cas 12069-32-8)08/02/2019
- Enhanced fracture toughness of Boron carbide (cas 12069-32-8) from microalloying and nanotwinning08/01/2019
- Uniaxial tensile strength and fracture analysis of a hot-pressed Boron carbide (cas 12069-32-8)07/31/2019
- Preparation of submicron Boron carbide (cas 12069-32-8) powder through gas-solid reaction method07/30/2019
- Properties of Boron carbide (cas 12069-32-8) ceramics made by various methods for use in ITER07/28/2019
-
Health and Chemical more >