Sonocatalytic reduction of nitrate using magnetic layered double hydroxide: Implications for removal mechanism

Add time:08/11/2019    Source:sciencedirect.com

In this study, magnetic layered double hydroxides (mag-LDHs) were synthesized through compositing magnetite with three different metals (Mg, Cu and Al) under ultrasound (US, 100 kHz frequency and 50 W power). For the first time, mag-LDHs were applied to sonocatalytic reduction of nitrate (NO3−) and the reduction mechanism were determined by conducting kinetic tests and various spectroscopic analyses. Based on the kinetic data, NO3− reduction and the selectivity for N2 highly depends on the ratio between Mg/Al, solution pH and sonication frequency. The best condition for sonocatalytic denitrification was found to be pH 7 operated under 100 kHz (50% power) using the catalyst with lowest amount of Al (mag-LDH-Al0.3Mg1.5). As a proposed mechanism, NO3− is initially reduced to NO2− by Cu0, and then further reduced to N2/NH4+ by Mg0. Hypothetically Al0 could provide sorption sites for hydrogen radicals (·H) dissociated from ultrasound, hence served as reducing sites in denitrification process. The XPS analysis showed an increased peak of Cu0 after the sonocatalytic reduction when catalyst has lower amount of Al. The excessive hydrogen adsorbed on Al0 might spill-over to the adjacent Cu, thus reducing the CuO into Cu0 at high temperature created by the implosion of the microbubbles. Without the use of consumable reducing agents (i.e. H2 gas), sonocatalytic reduction could be a potential candidate of remediation method to treat NO3− polluted water with high N2 selectivity and easy magnetic recovery.

We also recommend Trading Suppliers and Manufacturers of lead hydroxide nitrate (cas 12268-84-7). Pls Click Website Link as below: cas 12268-84-7 suppliers

Prev:Epoxy/layered double hydroxide (LDH) nanocomposites: Synthesis, characterization, and Excellent cure feature of nitrate anion intercalated Zn-Al LDH
Next:Enhanced adsorption of potassium nitrate with potassium cation on H3PO4 modified kaolinite and nitrate anion into Mg-Al layered double hydroxide)