Material CharacterisationCyclic uniaxial stress-strain test and rheological behavior of Carbon Black (cas 1333-86-4)/metakaolin dual-filler system used in nitrile rubber compounds
-
Add time:09/03/2019 Source:sciencedirect.com
Dual-filler systems may promote synergetic effects to mechanical properties in rubber compounds. The use of metakaolin (M) and carbon black (C) in nitrile rubber (NBR) compounds was studied with respect to rheological and non-obvious mechanical tests. The reaction order of the curing process was not influenced by the filler system, however, carbon black presented a slowdown effect in the vulcanization process. Cyclic uniaxial tests indicated that stress softening was observed even for unfilled compound; however, notably only-carbon black filled compound experienced the highest values for decrease in stress softening after second cycle. Although the polymer chains alone are the main driving force of hysteresis, it was more negatively affected by carbon black than by metakaolin. Moreover, dual filler composites experienced balanced results for stress softening, and other properties as Payne effect and complex viscosity.
We also recommend Trading Suppliers and Manufacturers of Carbon Black (cas 1333-86-4). Pls Click Website Link as below: cas 1333-86-4 suppliers
Prev:Properties of Carbon Black (cas 1333-86-4) produced by the thermal decomposition of methane in the products of premixed flames
Next:Black carbon emissions and regulatory policies in transportation) - 【Back】【Close 】【Print】【Add to favorite 】
- Related Information
- Development of a land use regression model for black carbon using mobile monitoring data and its application to pollution-avoiding routing09/05/2019
- Black carbon emissions and regulatory policies in transportation09/04/2019
- Properties of Carbon Black (cas 1333-86-4) produced by the thermal decomposition of methane in the products of premixed flames09/02/2019
- Full Length ArticleEffect of calcium and barium on potassium-catalyzed gasification of ash-free Carbon Black (cas 1333-86-4)09/01/2019
- The effect of Carbon Black (cas 1333-86-4) morphology to the thermal conductivity of natural rubber composites08/31/2019
- Atmospheric black carbon concentrations in Mexico08/30/2019
-
Health and Chemical more >